dc.contributor.author |
Barutcigil, Çağatay |
|
dc.contributor.author |
Barutcigil, Kubilay |
|
dc.contributor.author |
Kürklü, Duygu |
|
dc.contributor.author |
Harorlı, Osman Tolga |
|
dc.date.accessioned |
2016-10-24T10:29:44Z |
|
dc.date.available |
2016-10-24T10:29:44Z |
|
dc.date.issued |
2013 |
|
dc.identifier.citation |
Barutcigil, Ç. Barutcigil, K. Kürklü, D. Harorlı, O. Tolga (2013). Güncel dentin bağlayıcı ajanların ve uygulama yöntemlerinin makaslama bağlanma dayanımlarının karşılaştırılması.nönü Üniversitesi Sağlık Bilimleri Dergisi 2013; 2: 27-32 ss. |
tr_TR |
dc.identifier.uri |
https://www.inonu.edu.tr/uploads/old/3/260/27-32makale.pdf |
|
dc.identifier.uri |
http://hdl.handle.net/11616/4855 |
|
dc.description |
İnönü Üniversitesi Sağlık Bilimleri Dergisi 2013; 2: 27-32 ss. |
tr_TR |
dc.description.abstract |
Amaç: Bu çalışmanın amacı üniversal bağlayıcı ajanların makaslama bağlanma dayanımını farklı adeziv stratejilerde değerlendirmek ve
geleneksel bağlayıcı ajanlarla karşılaştırmaktır.
Gereç ve Yöntem: Yetmiş adet çürüksüz insan üçüncü büyük azı dişleri seçildi ve adezive ve uygulanacak stratejiye göre 7 gruba ayrıldı;
Single Bond Universal self-etch (SBUSe) ve etch-and-rinse (SBUEr), All Bond Universal self-etch (ABUSe) ve etch-and-rinse (ABUEr),
Adper Single Bond 2 (ASB), Clearfil SE Bond (CSE) ve Futurabond M (FBM). Dişlerin üzerlerine restorasyonlar yapıldı ve 370C/24 saat
distile su içerisinde bekletildi. Makaslama bağlanma dayanımı testleri bir üniversal test cihazı yardımıyla 0.5 mm/dk. hızında gerçekleştirildi.
Elde edilen verilerin analizleri tek yönlü varyans analizi ve Duncan testi ile yapıldı (α=0.05).
Bulgular: SBU ve ABU adeziv sistemler için dentin yüzeyine fosforik asit uygulanması bağlanma dayanımı önemli derecede arttırmıştır.
FBM dışındaki self-etch stratejiler arasında istatistiksel olarak bir fark bulunmadı. Tüm adeziv sistemler içersinde en düşük MPa değerleri
FBM göstermiştir (p<0.05).
Sonuç: Bu çalışmanın sonuçları doğrultusunda bu yeni tür üniversal bağlayıcı ajanların etch-and-rinse olarak tercih edilebilir. |
tr_TR |
dc.description.abstract |
Objective: The aim of this study was to evaluate the shear bond strength of universal adhesive under different strategies and to compare with
the conventional bonding systems.
Methods: Seventy sound human third molars selected and divided into 7 groups according to the adhesive and strategy: Single Bond
Universal self-etch (SBUSe) and etch-and-rinse (SBUEr), All Bond Universal self-etch (ABUSe) and etch-and-rinse (ABUEr), Adper Single
Bond 2 (ASB), Clearfil SE Bond (CSE) and Futurabond M (FBM). Build-ups were constructed and specimens were stored in distilled water
(370C/24h). Shear bond strength test were performed with a universal test machine at a crosshead speed of 0.5 mm/min. Data were analyzed
with one-way ANOVA and Duncan test (α=0.05).
Results: Prior to phosphoric acid etching significantly increased bond strength of the SBU and ABU. There was no statistically a difference
between self-etch strategies SBUSe, ABUSe and CSE except FBM. FBM showed the lowest mean MPa in all adhesives (p<0.05).
Conclusion: It can be concluded that using of the new class of universal adhesives as etch-and-rinse should be preferred. |
tr_TR |
dc.language.iso |
tur |
tr_TR |
dc.publisher |
İnönü Üniversitesi Sağlık Bilimleri Dergisi |
tr_TR |
dc.rights |
info:eu-repo/semantics/openAccess |
tr_TR |
dc.subject |
Kayma mukavemeti |
tr_TR |
dc.subject |
Dentin bağlayıcı ajanlar |
tr_TR |
dc.subject |
Shear bond strength |
tr_TR |
dc.subject |
Dentin bonding agents |
tr_TR |
dc.title |
Güncel dentin bağlayıcı ajanların ve uygulama yöntemlerinin makaslama bağlanma dayanımlarının karşılaştırılması |
tr_TR |
dc.title.alternative |
Comparison of shear bond strength of current dentin bonding agents and strategies |
tr_TR |
dc.type |
article |
tr_TR |
dc.relation.ispartof |
İnönü Üniversitesi Sağlık Bilimleri Dergisi |
tr_TR |
dc.department |
Akdeniz Üniversitesi Diş Hekimliği Fakültesi Restoratif Diş Tedavisi |
tr_TR |
dc.authorid |
TR20491 |
tr_TR |
dc.authorid |
TR194246 |
tr_TR |
dc.authorid |
TR117635 |
tr_TR |
dc.identifier.volume |
2 |
tr_TR |
dc.identifier.issue |
2 |
tr_TR |
dc.identifier.startpage |
27 |
tr_TR |
dc.identifier.endpage |
32 |
tr_TR |